The article presents the results of research on the finishing of M63 Z4 brass by vibratory machining. Brass alloy was used for the research due to the common use of ammunition elements, cartridge case and good cold forming properties on the construction. Until now, the authors have not met with the results of research to determine the impact of abrasive pastes in container processing. It was found that the additive for container abrasive treatment of abrasive paste causes larger mass losses and faster surface smoothing effects. The treatment was carried out in two stages: in the first stage, the workpieces were deburred and then polished. Considerations were given to the impact of mass of workpieces, machining time and its type on mass loss and changes in the geometric structure of the surface. The surface roughness of machining samples was measured with the Talysurf CCI Lite optical profiler. The suggestions for future research may be to carry out tests using abrasive pastes with a larger granulation of abrasive grains, and to carry out tests for longer processing times and to determine the time after which the parameters of SGP change is unnoticeable.
The article presents an example of finishing treatment for aluminum alloys with the use of vibration machining, with loose abrasive media in a closed tumbler. For the analysis of selected properties of the surface layer prepared flat samples of aluminum alloy PA6/2017 in the state after recrystallization. The samples in the first stage were subjected to a treatment of deburring using ceramic media. In a second step polishing process performed with a strengthening metal media. In addition, for comparative purposes was considered. only the case of metal polishing. The prepared samples were subjected to hardness tests and a tangential tensile test. As a result of finishing with vibratory machining, it was possible to remove burrs, flash, rounding sharp edges, smoothing and lightening the surface of objects made. The basic parameters of the surface geometry were obtained using the Talysurf CCI Lite - Taylor Hobson optical profiler. As a result of the tests it can be stated that the greatest reduction of surface roughness and mass loss occurs in the first minutes of the process. Mechanical tests have shown that the most advantageous high values of tensile strength and hardness are obtained with two-stage vibration treatment, - combination of deburring and polishing. Moreover the use of metal media resulted in the strengthening of the surface by pressure deburring with metal media.